铝板大家应该已经不算陌生了，毕竟在我们日常生活中到处可以看到铝板的身影，今天无锡铝板厂家的小编进来为大家分享一些避免铝板在生产过程中被划伤的注意事项。铝板是在铝板加工过程中添加各种合金元素(主要合金元素为铜、硅、镁、锌、锰、镍、铁、钛、铬、锂等)，以提高铝板的机械性能和化学指标。合金铝板具有纯铝板所不具备的一些特殊性能，广泛应用于船舶、冰箱、模具、航天设备等特殊环境中。

Aluminum plates are no longer unfamiliar to everyone, as they can be seen everywhere in our daily lives. Today, the editor from Wuxi aluminum plate manufacturer will share with you some precautions to avoid scratches on aluminum plates during the production process. Aluminum plate is made by adding various alloy elements (mainly copper, silicon, magnesium, zinc, manganese, nickel, iron, titanium, chromium, lithium, etc.) during the processing of aluminum plate to improve its mechanical properties and chemical indicators. Alloy aluminum plates have some special properties that pure aluminum plates do not possess, and are widely used in special environments such as ships, refrigerators, molds, aerospace equipment, etc.

合金铝板在生产加工过程中，很容易出现各种疤痕。线条。疤痕的原因有很多。需要多方面注意

Alloy aluminum plates are prone to various scars during the production and processing process. Lines. There are many reasons for scars. Attention needs to be paid to multiple aspects

铝板表面划伤的原因。

The reason for scratches on the surface of the aluminum plate.

划伤.擦伤.碰伤。

Scratches, abrasions, and bumps.

合金铝板在生产过程中，这些偏析浮出物或硬工业铝型材颗粒附着在工作带表面或损坏工作带，终划伤型材表面。

During the production process of alloy aluminum sheets, these segregation floats or hard industrial aluminum profile particles adhere to or damage the surface of the work strip, ultimately scratching the surface of the profile.

合金铝板模具或工作带上有杂物，模具工作带硬度较低，使工作带表面在挤压时划伤铝板

There are debris on the alloy aluminum plate mold or work strip, and the hardness of the mold work strip is low, causing scratches on the aluminum plate surface during extrusion

在出料轨道或床上有裸露的铝或石墨条，当与铝接触时，会划伤合金铝板表面

There are exposed aluminum or graphite strips on the discharge track or bed, which can scratch the surface of the alloy aluminum plate when in contact with aluminum

在床上人为拖动合金铝板造成擦伤

Scratches caused by manually dragging alloy aluminum plates on the bed

合金铝板在运输过程中相互摩擦或挤压，造成损坏。

Alloy aluminum plates may cause damage due to friction or compression during transportation.

解决铝板表面划伤的办法。

A solution to scratches on the surface of aluminum plates.

合金铝板模具上的工作带需要打磨光滑，挤压模具的空刀是否足够，表面是否光滑。

The working strip on the alloy aluminum plate mold needs to be polished smooth, whether the empty blade of the extrusion mold is sufficient, and whether the surface is smooth.

在生产合金铝板的过程中，注意模具线的产生。一旦产生线条，需要及时下模停止生产。

During the production of alloy aluminum plates, pay attention to the generation of mold lines. Once a line is produced, it is necessary to immediately stop production by lowering the mold.

在铝板锯切过程中：每次锯切都要及时清理锯切锯末。防止二次划伤。

During the aluminum plate sawing process, it is necessary to clean the sawdust in a timely manner every time it is sawed. Prevent secondary scratches.

同样，在数控加工铝板的过程中，还需要防止夹具上残留的铝渣划伤。

Similarly, in the process of CNC machining aluminum plates, it is also necessary to prevent scratches from residual aluminum slag on the fixture.

在出料轨道或床上有裸露的工业铝型材或石墨条，应避免硬杂物与铝板接触时划伤铝板表面

Exposed industrial aluminum profiles or graphite strips on the discharge track or bed should be avoided from scratching the surface of the aluminum plate when hard debris comes into contact with the aluminum plate

在生产搬运过程中要轻轻放置，尽量避免随意拖动或翻转合金铝板

During the production and transportation process, it is important to place the alloy aluminum plate gently and avoid dragging or flipping it randomly as much as possible

合理放置铝板，尽量避免相互摩擦。

Reasonably place aluminum plates and try to avoid friction with each other.

感谢您的阅读，此文的文章来源：铝板生产厂家更多的内容和问题请点击：我们会继续努力的为您提供服务，感谢您的支持！

Thank you for reading. The source of this article is aluminum plate manufacturers. For more information and questions, please click: We will continue to work hard to provide you with services. Thank you for your support!