铝卷厂家介绍铝卷上色过程：
Aluminum coil manufacturers introduce the process of aluminum coil coloring
1、预处理,先运用方法对外表进行清洗,运用物理和化学方法都能够,主要的就是使铝卷.这样是有利于氧化的完整的进行的,构成的氧化膜也会是细密的.预处理还能够运用一些机械设备处理.
1. Pretreatment, the use of methods to clean the external surface, the use of physical and chemical methods can, the most important is to make aluminum coil. This is conducive to the complete oxidation, the composition of the oxide film will be fine. Pretreatment can also use some mechanical equipment
2.阳极氧化,铝卷厂家通过与处理之后的铝卷,使基体发作阳极氧化反应,然后就是会生成细密的氧化薄膜.
2. Anodizing: aluminum coil manufacturers will react with the aluminum coil after treatment to form a fine oxide film

3.封孔,通过阳极氧化之后,氧化薄膜上会呈现许多的膜孔,封孔就是使这些膜孔关闭,防止氧化膜被污染.这种氧化膜是通明的,并且是具有吸附性的,这样就会在孔内堆积一些金属盐,这样就能在外表显显露一些正本的银白色,或者是之外的许多颜色.
3. Sealing, after anodizing, there will be many film holes on the oxide film. Sealing the hole is to close these film holes and prevent the oxide film from being polluted. This kind of oxide film is transparent and has adsorption, so some metal salts will be accumulated in the hole, so that some original silver white or many other colors can be displayed on the surface
铝卷生产厂家
Aluminum coil manufacturer
铝卷假设要投入运用，要在正常的温度下，温度不能过热也不能太严寒，假设作为屋面，高度不得低于10度。在装置之前，及时进行检查，保证屋面的资料没有磨损的表象，保证能够正常的运用，在正常的情况下保证运用的寿命。铝卷厂家螺栓头要用防水性强的物质密封，防止雨水进入生锈。
The aluminum coil is supposed to be put into use. The temperature should not be too hot or too cold under the normal temperature. It is assumed that as the roof, the height should not be less than 10 degrees. Before installation, timely inspection shall be carried out to ensure that there is no appearance of wear and tear on the roof data, so as to ensure normal operation and service life under normal conditions. The bolt head of aluminum coil manufacturer shall be sealed with waterproof material to prevent rainwater from entering and rusting.

铝卷加工的环境温度应在7℃以上，要根据铝卷厚度调整加工辊系的空隙，并铲除辊面及托板上的异物;一起要检查铝卷双面是不是脱漆，如脱漆，应查明原因且采纳办法后才干继续加工。
The ambient temperature of aluminum coil processing should be above 7 ℃. The gap of processing roller system should be adjusted according to the thickness of aluminum coil, and the foreign matters on the roller surface and support plate should be removed. It is necessary to check whether the paint on both sides of the aluminum coil is peeling off. If the paint is removed, the reason should be found out and the method should be adopted before continuing the processing.